Phenolic polymer prepared from o-cresol

ABSTRACT

Phenolic polymers which can be produced by reacting ortho-cresol with other phenolic materials, such as phenol, are described. Phenolic compositions comprising these phenolic polymers mixed with other phenolic materials, cellular materials produced from these phenolic polymers having low friability, and related processes and products are also described.

This is a divisional of application Ser. No. 509,565, filed Sept. 27, 1974, which is now U.S. Pat. No. 3,953,645, and which in turn was a divisional of application Ser. No. 354,636, filed Apr. 26, 1973, now U.S. Pat. No. 3,876,620.

Phenolic polymers have been known for decades. More recently there has been increased interest in phenolic polymers which can be formed into cellular material more commonly referred to as foams. See for example Thomas et al U.S. Pat. No. 2,744,875 (1965); Nelson Canadian Pat. No. 674,181 (1963); Dijkstra Canadian Pat. No. 684,388 (1964); Wissenfels et al Canadian Pat. No. 866,867 (1971); United Kingdom Specification No. 598,642 (1948); and Australian Pat. No. 128,508 (1945). A number of the cellular materials described in these and in other patents exhibit advantageous properties of compressive strength, self-extinguishing character, and low thermal conductivity. However, known cellular materials produced from phenolic polymers exhibit an undesirably high friability. This undesirably high friability is accompanied by increased dustiness and low tensile strength. In fact, this undesirably high friability has practically precluded the use of phenolic polymers as structural laminates such as wallboard. See also Modern Plastics Encyclopedia Volume 41, pages 362-363 (1964).

Accordingly, it is an object of the present invention to provide an improved phenolic polymer substantially free of the disdvantages of prior polymers.

Another object is to provide an improved phenolic polymer, an improved phenolic composition employing the phenolic polymer, an improved process for producing both the phenolic polymer and the phenolic composition, improved cellualr materials employing the phenolic polymer, an improved process for producing such cellular materials and an improved laminated building panel employing phenolic polymers.

A further object of the present invention is to provide a phenolic polymer which, when formed into a cellular product, exhibits a low friability generally less than .and preferably less than 10%.

A still further object is to provide an improved phenolic polymer which, when formed into a cellular material, exhibits low friability without adversely affecting compressive strength, its self-extinguishing character, and/or its thermal conductivity.

Additional objects and advantages of the present invention will be apparent to those skilled in the art by reference to the following detailed description and drawings wherein:

FIG. 1 is a cross-sectional view of a laminated building panel having one facing sheet; and

FIG. 2 is a cross-sectional view of a laminated building panel having two facing sheets.

According to the present invention, there is provided an improved alkylol group containing phenolic polymer of Formula I: ##STR1## wherein R¹ is ##STR2## hydrogen, or a radical of Formula II: ##STR3## The R² 's are independently selected from the group consisting of lower alkyl, phenyl, benzyl, halo, nitro, and hydrogen. The R³ 's are independently selected from the group consisting of ##STR4## hydrogen, or a radical of Formula II.

The R⁴ 's are independently selected from the group consisting of lower alkyl, hydrogen, phenyl, benzyl, or furyl. By furyl is meant the radical introduced by the use of furfural. In Formula I, m is an integer from 2 to 10 inclusive and is preferably an integer from 2 to 6 inclusive. When m is less than 2, a foam produced from such a phenolic polymer tends to have too high a friability. On the other hand, as m exceeds 10, the viscosity of the polymer increases to the point where it is difficult to produce the foam. The phenolic polymers of the present invention generally have a molecular weight between 200 and 2,000 and preferably have a molecular weight between 300 and 1500. At lower molecular weights, the resultant foams tend to have too high a friability, whereas at high molecular weights the viscosity of the phenolic polymer, even when a solvent is present, tends to be too high to permit processing within a reasonable time.

A preferred subclass of phenolic polymers are those of Formula III: ##STR5##

In Formula III, R¹ is HOCH₂ --, hydrogen, or a radical of Formula IV: ##STR6##

The R³ 's are independently selected from the group consisting of HOCH₂ --, hydrogen, or a radical of Formula IV.

In a preferred embodiment of the present invention, at least one of the R³ 's is methylol, i.e. HOCH₂ --. This is to ensure that there will be cross-linking sites on the phenolic polymer. Of course, such methylol groups or, when the aldehyde is other than formaldehyde, alkylol groups, are automatically introduced into the polymer as is well-known in the art by the process described below.

In the broadest aspects of the present invention, the phenolic polymer can contain widely varying ratios of the radicals of Formula II or IV to orto-cresol units. However, this ratio is generally from 1:3 to 3:1 and is preferably from 1:1.5 to 1.5:1. At lower ratios, i.e. a deficiency of radicals of Formula II or IV, the resultant cellular product cellular product tends to be too soft, probably by virtue of decreased cross-linking, whereas at higher ratios, i.e. deficiency of ortho-cresol, the cellular material produced from such a phenolic polymer, tends to be too friable. In determining the above ratios, one must include the radicals of Formula II or IV present in Formula I or III respectively.

PHENOLIC COMPOSITION

According to another aspect of the present invention, there is provided an improved phenolic composition which can be reacted to form the cellular material of the present invention. These phenolic compositions comprise the phenolic polymer of Formula I or Formula III, together with a compound of Formula V: ##STR7##

The compound of Formula V can be present in the phenolic composition in widely varying ratios but is generally present in a weight ratio of b 1:30 to 1:2 and is preferably present in a weight ratio of 1:20 to 1:5. Examples of suitable compounds of Formula V include among others: m-cresol, m-chlorophenol, m-nitrophenol, 3,5-xylenol, and phenol, i.e. hydroxy benzene. Phenol is the most preferred compound of Formula V because of cost, availability, and reactivity.

PROCESS

The phenolic polymers of Formula I and Formula III are produced according to the present invention by combining certain reactants in a two-step process. In this process, Step I must be practiced before Step II. It has been found that practicing the steps in the reverse order does not result in polymers of the present invention. Likewise, practicing the process of the present invention as a single step process wherein the ortho-cresol and the compound of Formula V are added simultaneously does not result in phenolic polymers from which can be produced cellular materials having the herein described low friability.

In Step I of the process of the present invention, ortho-cresol is reacted with an aldehyde of Formula VI: ##STR8## to produce an intermediate product of Formula VII: ##STR9## wherein R⁵ is hydrogen or ##STR10##

In step II, the intermediate product of Formula VII is reacted with an additional amount of the same or a different aldehyde of Formula VI and with a compound of Formula V. The resultant reaction product is a phenolic polymer of Formula I or, when the compound of Formula V is phenol, the resultant product is a polymer of Formula III. Step I can be practiced at widely varying temperatures from below 30° C to about 150° C but is generally practiced within these temperature limits and preferably between 60° C and 100° C. Step I can be practiced at sub-atmospheric pressure or super-atmospheric pressure but is generally practiced at atmospheric pressure for convenience. In certain industrial applications of the process of the present invention, it may be advantageous to practice Step I at reduced pressure in order to remove water of condensation which is produced during the reaction. In Step I the molar ratio of aldehyde of Formula VI to ortho-cresol can vary widely but is generally between 0.5:1 and 5:1 and preferably between 1:1 and 3:1. At lower ratios there is insufficient aldehyde to react with the ortho-cresol. Molar ratios in excess of 5:1 do not adversely affect Step I but introduce into the reaction vessel unnecessary aldehyde which may have to be removed for reasons explained more completely below. Selection of temperatures and pressures for Step II employs the same considerations as those of Step I. The aldehyde present in Step II can be separately or can be the residual aldehyde left from Step I. The total amount of aldehyde provided to the reaction in both Steps I and II is critical to optimum practice of the process of the present invention and it must be present in a site ratio of 1:0.40 to 1:0.75 and preferably in a site ratio of 1:0.46 to 1:0.60. In calculating the site ratio, it may be assumed that the ortho-cresol has two sites, i.e. reactive sites, and that the compound of Formula V has three reactive sites. The site ratio is defined as the quantity (two times the moles of o-cresol plus three times the moles of compound of Formula V) all divided the moles of aldehyde. The site ratio is normally expressed as a ratio, i.e. 1:0.40, rather than as a fraction, i.e. 1/0.40, or as a whole number, i.e. 2.5. This ratio means moles site : moles aldehyde.

According to an important aspect of the present invention, it is possible to produce the above-described phenolic compositions directly in one vessel concurrently with the synthesis of the phenolic polymers of the present invention. This is possible provided the above-described site ratios are maintained and provided that the compound of Formula V is present in the above-described ratio and provided the ratio of radicals of Formula IV or II to o-cresol is within the herein-described limits.

Step I of the process of the present invention can be practiced with either acidic or basic catalysts. Stated differently, the intermediate product of Formula VII can be produced either in the form of a Resole or in the form of a Novolak. On the other hand, it has been found that Step II must be practiced in the presence of a basic catalyst, i.e. as a Resole. Examples of suitable basic catalysts include, among others, sodium hydroxide, potassium hydroxide, calcium hydroxide, and barium hydroxide. Sodium hydroxide is preferred because of the solubility of sodium acetate formed when the catalyst is neutralized in a subsequent reaction step.

Examples of suitable acidic catalysts include, among others, HCl; H₃ PO₄ ; H₂ SO₄ ; arylsulfonic acids such as benzene sulfonic acid and toluene sulfonic acid.

After practicing Step II of the process, it is conventional to neutralize the basic catalyst. Any mineral or organic acid can be employed to neutralize the basic catalyst. Examples of suitable acids include, among others, acetic acid, oxalic acid, lactic acid, trichloroacetic acid, benzene sulfonic acid, toluene sulfonic acid, xylene sulfonic acid, hydrochloric acid, sulfuric acid, and phosphoric acid. The preferred acid is acetic acid because its reaction product with sodium hydroxide is sodium acetate. Sodium acetate is soluble in the phenolic polymer of the present invention and therefore does not have to be removed by filtration. On the other hand, oxalic acid can be employed if the resultant sodium oxalate is filtered from the reaction product.

In Steps I and II the catalyst is employed in an amount sufficient to catalyze the reaction and is generally present in molar ratios of 1:10 to 1:160 and preferably 1:40 to 1:80 moles of catalyst per total moles of o-cresol and phenolic compound of Formula V. At lower ratios the reaction time is uneconomically slow, whereas at higher ratios there is no attendant benefit and the reaction becomes difficult to control.

ALDEHYDES

In the broadest aspects of the present invention, any aldehyde can be employed. Examples of suitable aldehydes include among other furfural, benzaldehyde, and acetaldehyde. Formaldehyde is the preferred aldehyde. Formaldehyde can be employed in widely varying forms such as the 37% aqueous solution widely known as formalin. However, it is generally necessary to remove from the polymeric material the water introduced with the formalin. Formaldehyde is preferably employed in the form of paraformaldehyde which contains much less water.

CELLULAR MATERIAL

The cellular material of the present invention is formed by simply reacting the alkylol group containing phenolic polymer of Formula I or Formula III and the compound of Formula V under conditions such that a cellular product will result. As is well known in the phenolic foam art, the reaction can be conducted in the presence of a foaming catalyst, a blowing agent, and a surfactant. The cellular materials of the present invention generally have a conductivity, k value, of from 0.1 to 1.0 and preferably from 0.1 to 0.3 BTU-inch/Hr-° F-sq. ft.

FOAMING CATALYST

In the broadest aspects of the present invention, any catalyst which will enhance the cross-linking and foaming reaction can be employed in the present invention. However, the preferred foaming catalysts are aromatic sulfonic acids, examples of which include, among others, benzene sulfonic acid, toluene sulfonic acid, xylene sulfonic acid, and phenol sulfonic acid. Phosphoric acid can also be employed either along or in admixture with the sulfonic acids. The preferred sulfonic acid is a mixture of equal parts by weight of toluene sulfonic acid and xylene sulfonic acid as described in Mausher et al. U.S. Pat. No. 3,458,449. Another foaming catalyst which has been found to give excellent results is a blend of toluene sulfonic acid, phosphoric acid, and water in a weight ratio of 35-50:50-335:15.

The catalyst is generally present in the minimum amount that will give the desired cream times of 10 to 50 seconds and firm times of 40 to 500 seconds to the reacting mixture. The catalyst, however, generally comprises from 0.5 to 20, and preferably coprises from 1.0 to 15, weight percent based on the weight of the cellular material.

THE BLOWING AGENT

Any blowing agent characteristically employed in similar prior art products can be employed in the composition of the present invention. In general, these blowing agents are liquids having an atmospheric pressure boiling point between minus 50° and 100° C and preferably between zero and 50° C. The preferred liquids are hydrocarbons or halohydrocarbons. Examples of suitable blowing agents include, among others, chlorinated and fluorinated hydrocarbons such as chloroform, trichlorofluoromethane, CCl₂ FCClF₂, CCl₂ FCF₃, diethylether, n-pentane, cyclopentane, and 2-methylbutane. Trichlorofluoromethane is the preferred blowing agent. The blowing agents are employed in an amount sufficient to give the resultant foam the desired bulk density which is generally between 0.5 and 10, and, preferably between 1 and 5 pounds per cubic foot. The blowing agent generally comprises from 1 to 30, and preferably comprises from 5 to 20, weight percent of the composition. When the blowing agent has a boiling point at or below ambient, it is maintained under pressure until mixed with the other components. Alternatively, it can be maintained at subambient temperatures until mixed with the other components.

THE SURFACTANT

Successful results have been obtained with silicone/ ethylene-oxide/propylene-oxide copolymers as surfactants. Examples of suitable surfactants include, among others, alkoxy silanes, polysilylphosphonates, polydimethyl siloxane, and polydimethylsiloxane-polyoxyalkylene copolymers.

Examples of specific, commercially available surfactants useful in the present invention include, among others, polydimethylsiloxane-polyoxyalkylene block copolymers available from the Union Carbide Corporation under the tradename "L-5420" and "L-5340" and from the Dow Corning Corporation under the tradenames "DC-913" and "DC-195."

The surfactant generally comprises from 0.05 to 10, and preferably comprises from 0.1 to 6, weight percent of the phenolic composition. Non-ionic surfactants are generally preferred.

Referring now to the drawings, and in particular to FIG. 1, there is shown a laminated building panel 10 of the present invention. The building panel 10 comprises a single facing sheet 11 having thereon a cellular material 12 of the present invention. FIG. 2 shows a building panel 20 having two facing sheets 21 and 22 on either side of a cellular material 23.

Any facing sheet previously employed to produce building panels can be employed in the present invention. Examples of suitable facing sheets include, among others, those of kraft paper, aluminum, and asphalt impregnated felts, as well as laminates of two or more of the above.

Cream time is the time interval beginning with the addition of the catalyst and ending when the composition begins to rise. Unless otherwise indicated, the reactants are mixed under ambient conditions of atmospheric pressure and room temperature (25° C).

Firm time is the time interval between catalyst addition and the firm point. Firm time is measured by periodically pressing by hand the top of the rising foam with a tongue depresser (a stick approximately 6 inches × 3/4 inches × 1/16 inches). When the tongue depresser no longer penetrates the surface, the time is noted. The elapsed time from addition of catalyst to this point is termed the firm time.

Friability is the propensity of the foam to break expressed in percent weight loss. This is determined by the ASTM C-421 friability test conducted for 10 minutes.

The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. These non-limiting examples are illustrative of certain embodiments designed to teach those skilled in the art how to practice the invention and to represent the best mode contemplated for carrying out the invention.

EXAMPLE 1

This example is illustrative of the present invention.

The following quantities of the following ingredients are combined as illustrated.

    ______________________________________                                                          Quantity                                                      Item    Name           grams      gram-moles                                   ______________________________________                                         A      ortho-cresol    389        3.6                                          B      HCHO (93.6%     144        4.5                                                 paraformaldehyde)                                                       C      NaOH (50% solution)                                                                            7.2        0.09                                         D      HCHO            121        3.8                                          E      phenol          338        3.6                                          F      acetic acid     6          0.1                                          ______________________________________                                    

Items A, B, and C are reacted at 90° C for 4.75 hours in Step I to form a mixture. In Step II, items D and E are added to the mixture of Step I and the temperature is maintained at 90° C for 2 hours. Then Item F is added to neutralize to a pH of 5.0 to 7.0 and the reaction products are cooled to room temperature.

The items are calculated to be present in the following molar ratios:

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 HCHO: o-cresol, Step 1  1.25:1                                                 NaOH: (phenyl + o-cresol)                                                                              1:80                                                   ______________________________________                                    

The reaction products produced above had a viscosity of 17,000 centipoises at 25° C and constitute a phenolic composition of the present invention which analyzes as follows:

    ______________________________________                                         phenol            10.7   weight percent                                        cresol            0      weight percent                                        formaldehyde      0.15   weight percent                                        water             9.1    weight percent                                        phenolic polymer         balance                                               ______________________________________                                    

EXAMPLE 2

This example is illustrative of the present invention.

The following quantities of the following ingredients are combined as illustrated.

    ______________________________________                                                     Quantity                                                           Item  Name        grams        gram-moles                                      ______________________________________                                         A     ortho-cresol                                                                               1568         14.5                                            B     HCHO (92.5%)                                                                               707          21.7                                            C     NaOH (50%)  29.2         0.365                                           D     phenol      1364         14.5                                            E     HCHO        377          11.6                                            F     acetic acid 24           0.4                                             ______________________________________                                    

Items A, B, C, D, and E of Example 2 are reacted in the same order as in Example 1 except that Step I and Step II are maintained at 90° C for 2 and 2.5 hours respectively. Then F is added to the reactant mixture of Step II, followed by cooling to 50° C and maintaining at 50° C for 15 minutes. The reaction products cooled to room temperature.

The items are calculated to be present in the following molar ratios:

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 HCHO: o-cresol, Step 1  1.5:1                                                  NaOH: (phenol + o-cresol)                                                                              1:80                                                   ______________________________________                                    

The reaction product of Example 2 had a viscosity of 18,800 centipoises at 25° C and constitutes a phenolic composition of the present invention.

EXAMPLE 3

This example is of the present invention.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            grams      gram-moles                                   ______________________________________                                         A      ortho-cresol    392        3.63                                         B      HCHO (92.5%)    271        8.35                                         C      NaOH (50%)      7.3        .09                                          D      phenol          341        3.63                                         E      acetic acid     6          0.1                                          ______________________________________                                    

Items A, B, C, and D, are reacted at 90° C for 5 hours and then E is added to neutralize the product mixture to a pH of 6-8. Then the product mixture is cooled to room temperature.

The items are calculated to be present in the following ratios:

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 NaOH: (phenol + o-cresol)                                                                              1:80                                                   ______________________________________                                    

The polymer product of Example 3 is measured to have a viscosity of 17,000 centipoises at 25° C and constitutes a phenolic composition not representation of the present invention which analyzes as follows:

    ______________________________________                                         phenol             5.0 weight percent                                          cresol             7.0 weight percent                                          formaldehyde       0.2 weight percent                                          water              9.9 weight percent                                          phenolic polymer   balance                                                     ______________________________________                                    

EXAMPLE 4

This example is comparative of the present invention.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            grams      gram-moles                                   ______________________________________                                         A      ortho-cresol    392        3.63                                         B      HCHO (92.5%)    146        4.5                                          C      NaOH (50%)      7.3        0.09                                         D      HCHO (92.5%)    175        3.85                                         E      phenol          341        3.63                                         F      acetic acid     6          0.1                                          ______________________________________                                    

Items E and D are reacted in presence of C at 90° C for 3 hours in Step 1, followed by the addition of reactants A and B to the mixture of Step 1 to give a mixture of Step 2. The Step 2 is carried out at 90° C for 3.3 hours followed by neutralization with F to obtain a pH of 6.8.

The items are calculated to be present in the ratios given below:

                                      TABLE VI                                     __________________________________________________________________________     Run No.     AF-7                                                                               BW-6a                                                                             BW-6b                                                                              BW-6c                                                                              BW-7a                                                                              BW-7b                                                                              BW-7c                                                                              BW-8a                                                                              BW-8b                                                                              BW-8c                                                                              Bw-9a                                                                              BW-9b                   __________________________________________________________________________     Reinforcement, type.sup.(a)                                                                7TF                                                                               BW  BW  BW  BW      BW  BW  BW  BW  BW  BW                      Reinfocement, phr.sup.(b)                                                                  100                                                                               106 106 106 106     106 106 130 130 130 100 100                 FEF Carbon black, phr                                                                      29.4                                                                              29.4                                                                               29.4                                                                               29.4                                                                               40.0    40.0                                                                               40.0                                                                               29.4                                                                               29.4                                                                               29.4                                                                               55.0                                                                               55.0                Silane, wt.% of glass                                                                      -- 0.53                                                                               0.53                                                                               0.53                                                                               0.53    0.53                                                                               0.53                                                                               0.65                                                                               0.65                                                                               0.65                                                                               0.50                                                                               0.50                Cure time, minutes                                                                         15 15  30  60  15      30  60  14  30  60  15  30                  Shore hardness                                                                             88 83  88  89  85      88  90  84  89  90  89  91                  Elongation, %                                                                              110                                                                               132 57  52  141     36  30  139 56  34  120 51                  Tensile strength, psi                                                                      2162                                                                              1127                                                                               1614                                                                               2089                                                                               1494    1788                                                                               2335                                                                               1125                                                                               1606                                                                               2018                                                                               1652                                                                               2229                 at 100% elongation                                                                        2051                                                                              1013                                                                               --  --  1245    --  --  1009                                                                               --  13  1483                                                                               --                  Average tear                                                                    strength, lb/in                                                                           244                                                                               178 213 229 192     206 250 169 210 232 226 223                 __________________________________________________________________________      Notes:                                                                         .sup.(a) "7TF" means asbestos fiber, 7TF grade "BW" means B glass wool   

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 NaOH: (phenol + o-cresol)                                                                              1:80                                                   ______________________________________                                    

The phenolic composition produced in Step 2 has a viscosity of 17,400 centipoises. In this phenolic composition not representative of the present invention, the reaction of formaldehyde with phenol occurs first and the reaction of formaldehyde with o-cresol second. The resin analyzed as follows:

    ______________________________________                                         phenol            1.9    weight percent                                        cresol            15.3   weight percent                                        HCHO              0.2    weight percent                                        H.sub.2 O         9.8    weight percent                                        polymer                  Balance.                                              ______________________________________                                    

EXAMPLE 5

This example is illustrative of the present invention.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            grams      gram-moles                                   ______________________________________                                         A      ortho-cresol    389        3.6                                          B      HCHO (92.5%)    130        4.0                                          C      NaOH (50%)      14.4       0.18                                         D      HCHO            143        4.4                                          E      phenol          338        3.6                                          F      acetic acid     12         0.2                                          ______________________________________                                    

In Step 1 Items A, B, and C are reacted at 90° C for 4 hours and then at 100° C for 1 hour. In Step II the reaction mixture from Step I and reactants E and D are reacted at 90° C for 0.75 hours. Then reactant F is added to neutralize the product to a pH of 6.5.

The reactants are estimated to be in the following ratios:

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 HCHO: o-cresol,Step 1   1.1:1                                                  NaOH: (phenol + o-cresol)                                                                              1:40                                                   ______________________________________                                    

The reaction product of Example 5 is at a viscosity of 16,000 centipoises at 25° C and constitutes a phenolic composition of the present invention which analyzes as follows:

    ______________________________________                                         phenol            9.0    weight percent                                        cresol            0      weight percent                                        formaldehyde      0.5    weight percent                                        water             8.0    weight percent                                        phenolic polymer         Balance.                                              ______________________________________                                    

EXAMPLE 6

This example is illustrative of the present invention wherein Step I is acid catalyzed.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            gram       gram-moles                                   ______________________________________                                         A      ortho-cresol    389        3.6                                          B      HCHO (92.5%)    130        4.0                                          C      NaOH (50%)      14.4       0.18                                         D      HCHO            143        4.4                                          E      phenol          338        3.6                                          F      acetic acid     12.4       0.2                                          G      hydrochloric acid                                                                              0.6        --                                                  (concd.)                                                                ______________________________________                                    

In Step 1, Items A and G are mixed and warmed to about 70° C, then reactant B is added over a period of 2 hours followed by maintaining the temperature of the mixture at 90°-100° C for 0.5 hours. In Step II, the mixture from Step I and the reactants C, D and E are reacted at 90° C for 0.5 hours followed by neutralization with reactant F to obtain a pH of 6.6.

The reactants of Example 6 are calculated to be present in the following ratios:

    ______________________________________                                         phenol: o-cresol        1:1                                                    sites ratio             1:0.46                                                 HCHO: o-cresol,Step 1   1.1:1                                                  NaOH: (phenol + o-cresol)                                                                              1:40                                                   ______________________________________                                    

The resultant phenolic composition had a viscosity of 14,000 centipoises at 25° C.

EXAMPLES 7, 8, 9, 10 and 11

Resins were prepared as in Example 1, except that the sites ratio was varied from 1:0.40 to 1:0.75. Reaction times and viscosities are shown in Table I. All resins were neutralized with acetic acid.

    __________________________________________________________________________     RESIN PREPARATION AT VARIOUS SITES RATIOS                                      __________________________________________________________________________          Sites Ratio                                                                    (3(moles phenol)+                                                                        Step 1, Reaction time                                           Example                                                                             2(moles cresol):                                                                         Moles HCHO:                                                                            Hours     Viscosity,                                    No.  moles HCHO                                                                               Moles Cresol                                                                           Step 1                                                                              Step 2                                                                              cp at 25° C                            __________________________________________________________________________     7    1:.40     1.5     2    4.2  16,200                                        8    1:.50     1.25    5    1.75 21,200                                        9    1:.55     1.25    5    1.5  22,000                                        10   1:.60     1.5     2    3.5  14,800                                        11   1:.75     1.5     2    1.7  14,400                                        Resin Conditions:                                                              Reaction Temperature, ° C                                                                      90                                                      Mole Ratio Phenol : Ortho Cresol                                                                      1:1                                                     Moles NaOH: (Moles Phenol + Moles Cresol                                                              1:80                                                    __________________________________________________________________________

EXAMPLES 12, 13, 14, 15, 16 and 17

These resins were prepared as in Example 1, except the mole ratio of phenol to cresol was varied. All formaldehyde was added in Step I and catalyst ratio was increased to 1:40 to decrease the reaction time. Resin conditions and viscosities are compiled in Table II.

                                      TABLE II                                     __________________________________________________________________________     RESIN PREPARATION AT VARIOUS MOLE RATIOS FOR PHENOL TO CRESOL                  Step 1                                                                         __________________________________________________________________________             Moles Phenol:                                                                           Moles HCHO:                                                                            Reaction Time, Hrs.                                                                        Viscosity,                                Example No.                                                                            Moles Cresol                                                                            Moles Cresol                                                                           Step 1                                                                               Step 2                                                                               cp at 25° C                        __________________________________________________________________________     12      1:1.5    1.8     1.5   2.0   15,000                                    13      1:1      2.3     1.5   2.5   15,000                                    14      1.25:1   2.6     1.5   3.7   16,200                                    15      1.5:1    3.0     1.5   5     14,000                                    16      2:1      3.7     1.5   5.6   --                                        17      3:1      5.1     1.5   9.0   --                                        Resin Conditions:                                                              Sites Ratio              1:.46                                                 Moles NaOH:(Moles Phenol + Moles Cresol)                                                                1:40                                                  Reaction Temperature, ° C                                                                        90                                                    __________________________________________________________________________

EXAMPLE 18

This example is comparative of the present invention and is illustrative of a phenolic polymer containing no o-crescol.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            grams      gram-moles                                   ______________________________________                                         A      NaOH (50%)      7.2        0.09                                         B      HCHO (92.5%)    323        10                                           C      phenol          677        7.2                                          D      acetic acid     6          0.1                                          ______________________________________                                    

Items A, B, and C are mixed and maintained at 90° C for 3.8 hours. Then Item D is added to give a pH of 6.5 to the resin product.

The reactants are present in the following ratios:

    ______________________________________                                         Sites ratio             1:0.46                                                 NaOH : phenol           1:80                                                   ______________________________________                                    

The resin product had a viscosity of 37,000 centipoises at 25° C.

EXAMPLE 19

This example is illustrative of the present invention.

The following quantities of the following ingredients are combined as illustrated:

    ______________________________________                                                          Quantity                                                      Item   Name            grams      gram-moles                                   ______________________________________                                         A      ortho-cresol    1560       14.5                                         B      HCHO (92.5%)    707        21.7                                         C      NaOH (50%)      14.6       0.10                                         D      phenol          1364       14.5                                         E      HCHO            377        11.6                                         F      acetic acid     24         0.4                                          ______________________________________                                    

In Step I, Items A and B are reacted in the presence of C at 90° C for 4.25 hours to give a mixture. In Step II, the reaction mixture of Step I and Items D and E are mixed and maintained at 90° C for 4.25 hours. Then Item F is added, cooled to 50° C and maintained at 50° C for 15 minutes. Then the reaction mixture is allowed to cool to room temperature.

The reactants are present in the following ratios:

    ______________________________________                                         phenol : o-cresol       1:1                                                    sites ratio             1:0.46                                                 HCHO : o-cresol         1.5:1                                                  NaOH : (phenol + o-cresol)                                                                             1:160                                                  ______________________________________                                    

The resin product had a viscosity of 19,000 centipoises at 25° C.

EXAMPLE 20

This example illustrates the synthesis of foaming catalysts useful in the present invention.

The following quantities of the following ingredients are combined as indicated to produce Catalyst A:

    ______________________________________                                         Ingredients              Quantity                                              Item    Name                 grams                                             ______________________________________                                         A       p-toluene sulfonic acid                                                                             333                                               B       xylene sulfonic acids                                                                               333                                               C       water                333                                               ______________________________________                                    

Items A, B, and C are mixed. The resultant composition is termed Catalyst A.

The following quantities of the following ingredients are combined as indicated to produce Catalyst B:

    ______________________________________                                         Ingredients              Quantity                                              Item    Name                 grams                                             ______________________________________                                         A       Ultra TX             667                                               B       water                333                                               ______________________________________                                    

Items A and B are mixed. The resultant composition is termed Catalyst B. Ultra TX is a mixture of equal parts by weight of p-toluene sulfonic acid and xylene sulfonic acids available from the Witco Chemical Company.

EXAMPLE 21

This example illustrates the synthesis of a cellular material of the present invention.

The following quantities of the following ingredients are combined as indicated:

    ______________________________________                                         Ingredients              Quantity                                              Item     Name                grams                                             ______________________________________                                         A       phenolic polymer of Ex. 1                                                                           80                                                B       phenol               11                                                C       Catalyst B           13                                                D       CFCl.sub.3           10                                                E       polydimethyl siloxane                                                          polyalkylene oxide block                                                       copolymer            2                                                 F       Water                9                                                 ______________________________________                                    

Items A through F are mixed in an open vessel whereupon a reaction ensues. The cream times and firm times are noted and recorded in Table III. Several hours later the density and friability are determined and recorded in Table III. Items A, B and F are added together in the form of (100 g) of the phenolic composition of Example 1.

EXAMPLES 22 and 27

The procedure of Example 1 is repeated except that the phenolic composition of Example 1 is replaced successively by the phenolic compositions of Examples 2 through 6 and 18. The results are recorded in Table III.

                                      TABLE III                                    __________________________________________________________________________     Example No. 21   22   23   24  25   26   27                                    __________________________________________________________________________     Phenolic polymer from                                                          Example Number                                                                             1    2    3    4   5    6    18                                    Cream Time (sec.)                                                                          10-15                                                                               15-20                                                                               <5   <5  10-15                                                                               10-15                                                                               5-10                                  Firm Time (sec.)                                                                           180  150-180                                                                             120-150                                                                             120 200-240                                                                             180  240                                   Density (lb per cu-ft)                                                                     1.7  1.8  1.8  1.5 1.8  1.9  1.6                                   Friability (%)                                                                             8    8.5  19   60  15   15   55                                    Illustrative (I) or                                                                        I    I    C    C   I    I    C                                     Comparative (C)                                                                __________________________________________________________________________

By reference to Table III, it can be seen that cellular materials produced from phenolic polymers of the present invention, namely those of Examples 1, 2, 5 and 6, all exhibit low friability. On the other hand, cellular material produced from the phenolic polymer of Example 3 wherein Step I and Step II are practiced together has an undesirably high friability of 19 percent. Furthermore, the cellular material produced from the phenolic composition of Example 4 wherein Step II is practiced before Step I has an undesirably high friability of 60%. The comparative examples also exhibit an undesirably fast cream time. The cellular material produced from phenolic polymer of example which contains no difirmitional phenol also produced an undesirably high friability of 55%.

EXAMPLE 28

The phenolic composition of Example 1 is spread on a paper facing sheet and produces the laminated panel 10 of FIG. 1.

EXAMPLE 29

The phenolic composition of Example 2 is placed between two facing sheets each comprising an asphalt impregnated felt commonly used as a roofing membrane.

EXAMPLE 30

The example illustrates the present invention employing other suitable commercially available surfactants.

The procedure of Example 21 is repeated except that the surfactant (Item E) is replaced by the surfactant shown in Table IV with the results shown.

                                      TABLE IV                                     __________________________________________________________________________     SURFACTANT                        CELLULAR MATERIAL                            Name   Description   Manufacturer Friability (%)                                                                         Cell Structure                       __________________________________________________________________________     SF-1165                                                                               polydimethyl siloxane-                                                                       General Electric                                                                            9       small, uniform                              polyalkylene oxide block                                                       copolymer                                                               L-5340 same          Union Carbide                                                                               7       same                                 LK-221 organic copolymer                                                                            Houdry       8       same                                 EL-719 ethyoxylated vegetable oil                                                                   General Aniline & Film                                                                      9       same                                 Tween 40                                                                              polyoxyethylene                                                                              Atlas        7       medium,uniform                              sorbitan palmitate                                                      __________________________________________________________________________

Although the invention has been described in considerable detail with reference to certain preferred embodiments thereof, it will be undestood that variations and modifications can be effected within the spirit and scope of the invention as described above and as defined in the appended claims. 

What is claimed is:
 1. An alkylol group containing phenolic polymer of Formula I: ##STR11## wherein: a. R¹ is ##STR12## hydrogen or a radical of Formula II: ##STR13## b. the R² 's are independently selected from the group consisting of lower alkyl, phenyl, benzyl, halo, nitro and hydrogen,c. The R³ 's are independently selected from the group consisting of ##STR14## hydrogen or a radical of Formula II, wherein at least one of the R³ 's is alkylol, p1 d. the R⁴ 's are independently selected from the group consisting of lower alkyl, hydrogen, phenyl, benzyl, or furyl, e. m is an integer from 2 to 10 inclusive, f. the phenolic polymer has a molecular weight between 200 and
 2000. 2. The phenolic polymer of claim 1 wherein R² is hydrogen.
 3. The phenolic polymer of claim 1 wherein R⁴ is hydrogen.
 4. A methylol group containing phenolic polymer of claim 1 of Formula III: ##STR15## wherein: a. R¹ is HOCH₂ --, hydrogen, or a radical of Formula IV: ##STR16## b. the R³ 's are independently selected from the group consisting of HOCH₂ --, hydrogen, or a radical or Formula IV, wherein at least one of the R³ 's is methylol,c. m is an integer from 2 to 10 inclusive, d. the phenolic polymer has a molecular weight between 200 and
 2000. 5. A methylol group containing phenolic polymer of Claim 1 of Formula III: ##STR17## wherein: a. R¹ is HOCH₂ --, hydrogen or a radical of Formula IV: ##STR18## b. the R³ 's are independently selected from the group consisting of HOCH₂ --, hydrogen or a radical of Formula IV, with the proviso that at least on R³ is HOCH₂ --,c. m is an integer from 3 to 6 inclusive, d. the phenolic polymer has a molecular weight between 300 and 1500, e. the ratio of radicals of Formula IV to o-cresol units is 1:1.5 to 1.5:1.
 6. A composition of matter comprising:A. an alkylol group containing phenolic polymer of claim 1 of Formula I: ##STR19## wherein: a. R¹ is ##STR20## hydrogen, or a radical of Formula II: ##STR21## b. the R² 's are independently selected from the group consisting of lower alkyl, phenyl, benzyl, halo, nitro and hydrogen c. the R³ 's are independently selected from the group consisting of ##STR22## hydrogen, or a radical or Formula II, wherein at least one of the R³ 's is alkylol, d. the R⁴ 's are independently selected from the group consisting of lower alkyl, hydrogen, phenyl, benzyl, or furyl, e. m is an integer from 2 to 10 inclusive, f. the phenolic polymer has a molecular weight between 200 and 2000, and B. a compound of Formula V ##STR23## wherein the weight ratio of B-A is 1:30 to 1:2.
 7. A composition of matter of claim 6 comprising:A. a methylol group containing phenolic polymer of Formula III: ##STR24## wherein: a. R¹ is HOCH₂ --, hydrogen or a radical of Formula IV: ##STR25## b. the R³ 's are independently selected from the group consisting of HOCH₂ --, hydrogen or a radical of Formula IV, wherein at least one of the R₃ 's is methylol, c. m is an integer from 3 to 6 inclusive, d. the phenolic polymer has a molecular weight between 300 and 1500, and B. phenol, wherein the weight ratio of B:A is 1:20 to 1:5. 